ESTD PERPUSTAKAAN UNTAD
ESTD PERPUSTAKAAN UNTAD
| JudulPENGARUH WAKTU PERENDAMAN PADA DYE UBI UNGU TERHADAP KINERJA DYE SENSITIZED SOLAR CELL (DSSC) |
| Nama: WARDIANSYAH |
| Tahun: 2025 |
| Abstrak ABSTRAK Wardiansyah “Pengaruh Waktu Perendaman Pada Dye Ubi Ungu Terhadap Kinerja Dye Sensitized Solar Solar Cell (Dssc)” Dibimbing oleh Rustan Hatib dan Muchsin. Penelitian ini bertujuan untuk mengetahui pengaruh variasi waktu perendaman (6, 8, 12, 18, dan 24 jam) terhadap karakteristik dan performa Dye Sensitized Solar Cell (DSSC) berbasis pewarna alami dari ubi ungu (Ipomoea batatas L.). Karakterisasi dilakukan melalui analisis spektrum FTIR dan pola difraksi XRD, serta pengujian performa perangkat DSSC meliputi nilai tegangan rangkaian terbuka (Voc), arus hubung singkat (Isc), fill factor (FF), dan efisiensi (?). Hasil uji FTIR menunjukkan keberadaan gugus fungsi utama seperti –OH, C=O, dan C–H yang menandakan adanya senyawa antosianin dalam pewarna. Intensitas penyerapan tertinggi ditemukan pada waktu perendaman 12 jam, dengan bilangan gelombang kuat di 3283,14 cm?¹ (gugus –OH) dan 1634,09 cm?¹ (C=C aromatik). Hasil XRD menunjukkan pola kristal amorf dengan indikasi peningkatan ketertiban struktur pada perendaman 12 jam. Dari pengujian performa, DSSC dengan perendaman 12 jam menghasilkan efisiensi tertinggi sebesar 0,1648%, dengan Voc sebesar 0,430 V dan Isc sebesar 0,00084 A. Nilai ini menunjukkan peningkatan signifikan dibandingkan waktu perendaman lainnya. Dengan demikian, waktu perendaman 12 jam dinilai sebagai kondisi optimal dalam proses penyerapan pewarna alami ubi ungu, karena mampu memberikan interaksi maksimum antara pewarna dan permukaan semikonduktor TiO?, sehingga meningkatkan efisiensi konversi energi. Penelitian ini menunjukkan bahwa pewarna alami ubi ungu berpotensi sebagai sensitizer ramah lingkungan dalam pengembangan DSSC. Kata Kunci : DSSC, XRD,FTIR, Efisiensi, Dye, Ubi Jalar Ungu ABSTRAC Wardiansyah “The Effect Of Immersion Time In Purple Sweet Potato Dye On The Performance Of Dye Sensitized Solar Cell (Dssc)” Supervised by Rustan Hatib and Muchsin. This study aims to investigate the effect of immersion time variation (6, 8, 12, 18, and 24 hours) on the characteristics and performance of Dye-Sensitized Solar Cells (DSSC) based on natural dye extracted from purple sweet potato (Ipomoea batatas L.). Characterization was conducted through FTIR spectroscopy, XRD diffraction patterns, and performance testing, which included open-circuit voltage (Voc), short-circuit current (Isc), fill factor (FF), and overall efficiency (?). FTIR analysis confirmed the presence of key functional groups such as –OH, C=O, and C–H, indicating anthocyanin compounds in the dye. The highest absorption intensity was found at the 12-hour immersion time, particularly at 3283.14 cm?¹ (–OH group) and 1634.09 cm?¹ (aromatic C=C), suggesting strong dye bonding. XRD results revealed an amorphous crystal pattern, with improved structural ordering observed at the 12-hour treatment. Performance tests showed that the DSSC immersed for 12 hours achieved the highest efficiency of 0.1648%, with a Voc of 0.430 V and an Isc of 0.00084 A. These values represent a significant improvement compared to other immersion durations. Therefore, 12 hours of immersion is considered the optimal condition for natural dye absorption from purple sweet potato, as it promotes maximum interaction between the dye and TiO? semiconductor surface, enhancing energy conversion efficiency. This research demonstrates that purple sweet potato dye has promising potential as an eco-friendly sensitizer for DSSC development. Keywords : DSSC, XRD,FTIR, Efficiency, Dye, Purple Sweet Potato |